EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {1}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {2}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {3}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {4}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {1}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {2}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {3}
EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT {4}

EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT

$51.79 $73.99

EPOXY RESIN 1 GALLON KIT * CLEAR * UV RESISTANT * LAMINATING * FIBERGLASS * BOAT

Availability:
In Stock
  • Estimated Delivery:Oct 02 - Oct 09

  • Free Shipping & Returns: Free Shipping for all orders. Free Return

Guarantee safe & secure checkout

READ BEFORE USING THIS PRODUCT
Product is 2:1 Resin to Hardener Mix Ratio.
You will receive 2 parts resin to 1 part hardener.  Each kit makes the total amount of product listed once mixed together.
Covers 26ft2 @ 60mils or 1/16 inch.  
GENERAL
SC110 is a marine grade, 100% solids epoxy with UV protection additives that o ffer long term non-yellowing protection with non-blushing and non-chalking  properties.  SC110 adheres to wood, fiberglass, metal, stainless steel,  concrete, stone, canvas, glass and virtually anysurface with 13,500 psi  strength. SC110 preserves the substrate with an ultra-clear, scratch resistant  finish while remaining flexible enough to withstand vibration and  expansion/contraction. SC110 is a specially formulated 2-component epoxy with a  modified cycloaliphaticamine curative. SC110 combines a UV absorber coupled with
a hindered amine light stabilizer which inhibits degradation of the epoxy from  sunlight and protects the exterior with a glossy, glass-like finish that will  endure heavy traffic and extreme conditions.  SC110 bondschemically and  mechanically to the substrate and can be blended with dyes, silica, sands, wood  flowers, pebbles and other materials. SC110 forms a polished, highly durable,  wear resistant surface and is unaffected by saltwater, fuel, oil, and mild acids
while exhibiting long term corrosion proof and chemical resistance protection.  SC110 is used for boat building, fiberglass fabricating, wood working, bar top finishing and many other applications.
COMPONENTS  
SC110 is composed of a resin and hardener supplied in a 1, 3, 6, 12 or 15 gallon kits.
SC110 resin is a 100% solids no VOC, 2-component, self-leveling, primerless,  low odor, non-blushing epoxy that provides a sufficient work life, rapid track  free time and high adhesion to aggregates and pavements. Each kit includes both  pre-proportioned resin (part A) andhardener (part B) which are mixed at 2 parts  resin to 1 part hardener by volume. To use, the part B is added to the part A  and then mixed immediately prior to use. VOC = 0 g/l. Following are properties and specifications for SC110:
SC110 PROPERTIES AT 77°F (25°C) 
Properties
Typical
Test Method
Components
A) Resin, (B) Hardener
Mixed Density, lbs./gal. (kg/l)
9.2 (1.02)
Mix Ratio, pbv (pbw)
2/1(100:45)
Color
Clear
Mixed Viscosity, cP 77F
800
ASTM D2393 (D2196)
Work Time, minutes 100grams
60
ASTM C881
Peak Exotherm Temperature 100grams
136°F
Application Temperature, °F (°C)
Ideal
Acceptable
70-80 (21-27)
50-95 (10-35)
Coverage*, ft2/gal @20mils
80
Compressive Strength psi
13,500
ASTM D695
Tensile Strength, psi
7,503
ASTM D638
Elongation at Break, %
6
ASTM D638
Hardness, Shore D
78-85
ASTM D2240
Adhesion Strength @ 24hrs psi to concrete
780
ASTM D4541
Flexural Strength psi
12,800
ASTM D790
Water Absorption @24hrs., %
0.10
ASTM D570
Thermal Compatibility
Pass
ASTM C884
VOC g/l
0
Varies with surface porosity and texture.
APPLICATION  
Application of SC110 is summarized as follows.  The 2 components of the SC110  are mixed, and then uniformly applied at the desired thickness typically 20  mils to the cleaned and prepared surface.  SC110 will soft gel in 3 hours at 20mils and fully cure in 12 hours at 77°F.
CLEAN-UP
Use a mixture of MIBK and Butyl Acetate (50/50), Acetone or MEK for cleanup.   Skin may be cleaned with denatured alcohol, preferably rubbing alcohol.
Refer to the MSDS for further information.